Quartz Beaker
Zida: 99.99% galasi la quartz (SiO₂)
Njira: kudula, kupukuta, etching, kuika chizindikiro, etc.
MOQ: 20 ma PC
Kufotokozera
Zofunika Kwambiri
- Kukaniza Kwambiri kwa Thermal
- Superior Chemical Inertness
- Kuwala Kwambiri
- Kukula Kwamafuta Otsika
- Precision Manufacturing
Mapulogalamu
- Kugwiritsa Ntchito Laboratory
- Njira Zamakampani
- Kafukufuku & Analysis
- Kutentha Kwambiri{{0}Kugwira Ntchito
Kukula Kofanana Kwa Quartz Beaker
|
Kuchuluka (ml) |
Diameter Yakunja (mm) |
Kutalika (mm) |
Sikelo yotalikirapo(mm) |
Makulidwe a khoma (mm) |
|
5 |
22 |
30 |
- |
0.7 |
|
10 |
26 |
35 |
4 |
0.7 |
|
25 |
34 |
50 |
5 |
0.7 |
|
50 |
42 |
60 |
5 |
0.8 |
|
100 |
50 |
70 |
10 |
0.9 |
|
150 |
60 |
80 |
10 |
1.0 |
|
250 |
70 |
95 |
25 |
1.1 |
|
400 |
80 |
110 |
25 |
1.2 |
|
500 |
85 |
120 |
25 |
1.2 |
|
600 |
90 |
125 |
50 |
1.3 |
|
800 |
100 |
135 |
50 |
1.3 |
|
1000 |
105 |
145 |
50 |
1.3 |
|
2000 |
130 |
185 |
100 |
1.4 |
|
3000 |
150 |
310 |
100 |
1.7 |
|
5000 |
170 |
270 |
500 |
2.0 |
Katundu
|
Zakuthupi |
Makhalidwe |
|
Chiyero |
＞99.99% |
|
Kuchulukana |
2.2g/cm3 |
|
Kuwonekera |
＞90% |
|
Mohs Kuuma |
5.5--6.5 |
|
Deformation Point |
1280 digiri |
|
Softening Point |
1780 digiri |
|
Annealing Point |
1250 digiri |
|
Kutentha Kwambiri (20 - 350 digiri) |
670J/kg. digiri |
|
Thermal Conductivity (20 digiri) |
1.4W/m. digiri |
|
Kutentha kwapakati (w/mk,1000 digiri) |
1.0-1.2 |
|
Refractive Index |
1.4585 |
|
Coefficient of Thermal Expansion |
5.5*10 -7cm/cm. digiri |
|
Kutentha - Kutentha kogwira ntchito |
1750-2050 digiri |
|
Kutentha kwa Service kwakanthawi - |
1300 digiri |
|
Kutalika kwa - kwa Service Temperature |
1100 digiri |
|
Chemical Properties |
Makhalidwe |
|
Kusamva acid |
Asidi Wamphamvu (kupatula HF), Wamphamvu alkali, organic solution |
|
Kutentha kwambiri Kusamva dzimbiri |
Zabwino kwambiri |
|
Chitsulo Chosayera |
5 ppm |
|
Zida Zamagetsi |
Makhalidwe |
|
Kukaniza |
7 * 107Ω.cm |
|
Mphamvu ya Insulation |
250 ~ 400Kv/cm |
|
Dielectric Constant |
3.7~3.9 |
|
Dielectric Absorption Coefficient |
＜4*10-4 |
|
Dielectric Loss Coefficient |
＜1*10-4 |
|
Mechanical Properties |
Makhalidwe |
|
Compressive Mphamvu |
1100MPa |
|
Kupindika Mphamvu |
ku 67MPa |
|
Kulimba kwamakokedwe |
48MP pa |
|
Chiwerengero cha Poisson |
0.14~0.17 |
|
Young's Modulus |
72000MPa |
|
Shear Modulus |
31000MPa |
FAQ
Q1: Kodi ma beak a quartz angagwiritsidwe ntchito ndi hydrofluoric acid (HF)?
A: Ayi! Quartz imachita ndi HF. Gwiritsani ntchito PTFE kapena HF-njira zina zosamva.
Q2: Kodi quartz ikuyerekeza bwanji ndi galasi la borosilicate?
A: Quartz imakhala ndi kutentha kwapamwamba kwambiri (~ 1200 digiri vs. ~ 500 digiri) komanso kuwonekera bwino kwa UV.
Q3: Kodi ma beaker a quartz awa ndi otheka?
A: Inde, amapirira autoclaving (nthawi zambiri mpaka 200 digiri pansi pa kukakamizidwa).
Q4: Kodi mumapereka kukula kwake kapena mawonekedwe?
A: Inde! Lumikizanani nafe zopempha za OEM/ODM (mwachitsanzo, ma spouts, zogwirira, zolembera).
Q5: Kodi nthawi yotsogolera yamaoda ambiri ndi iti?
A: Nthawi zambiri zimatengera kuchuluka (zofotokozera zomwe zilipo).
Hot Tags: beaker ya quartz, China opanga ma beaker a quartz, ogulitsa, fakitale
Tumizani kufufuza
Muthanso Kukonda